International Grade | China Grade | C Carbon | Cr Chromium | Mn Manganese | Si Silicon | Mo Molybdenum | V Vanadium | Co Cobalt | S Sulphur | P Phosphorus | Ni Nickel | N |
---|---|---|---|---|---|---|---|---|---|---|---|---|
1.4116 | JXS05-15MoV | 0.45-0.55 | 14.00-15.00 | ≦1.00 | ≦1.00 | 0.50-0.80 | 0.10-0.20 | ≦0.030 | ≦0.035 | |||
6Cr14 | JXS06-14 | 0.65-0.70 | 13.00-14.00 | ≦1.00 | ≦1.00 | ≦0.030 | ≦0.035 | |||||
AUS6 | JXS06-14MoV | 0.58-0.65 | 13.00-14.00 | ≦1.00 | ≦1.00 | 0.10-0.30 | 0.10-0.20 | ≦0.030 | ≦0.035 | |||
AUS10 | JXS10 | 0.95-1.1 | 13.00-14.00 | ≦1.00 | ≦1.00 | 0.10-0.30 | 0.10-0.20 | ≦0.030 | ≦0.035 | |||
AUS10Co | JXS10Co | 0.95-1.1 | 13.00-14.00 | ≦1.00 | ≦1.00 | 0.20-0.25 | 0.10-0.20 | 0.15-0.25 | ≦0.030 | ≦0.035 | 0.05-0.12 | |
9Cr13MoVCo | JXS09-13Co | 0.88-0.95 | 13.00-14.00 | ≦0.80 | ≦0.80 | 0.10-0.30 | 0.10-0.20 | 0.15-0.25 | ≦0.030 | ≦0.035 | ||
SUS440A | 7Cr17MoV | 0.65~0.70 | 16.40~17.10 | 0.40~0.80 | ≤1.00 | 0.50~0.60 | 0.10~0.30 | ≤0.01 | ≤0.02 | ≤0.40 | ||
SUS440B | 8Cr14MoV | 0.75~0.80 | 13.50~14.50 | 0.20~0.80 | ≤0.80 | 0.40~0.50 | 0.10~0.30 | ≤0.04 | ≤0.03 | ≤0.60 | ||
9Cr14MoV | 0.88~0.92 | 13.50~14.50 | 0.20~0.80 | ≤0.80 | 0.40~0.50 | 0.10~0.30 | ≤0.04 | ≤0.03 | ≤0.60 | |||
9Cr14MoV+Co | 0.88~0.92 | 13.50~14.50 | 0.20~0.80 | ≤0.80 | 0.40~0.50 | 0.10~0.30 | 0.20~0.30 | ≤0.04 | ≤0.03 | ≤0.60 | ||
SUS440C | 9Cr18MoV (SUS440C) Kitchen knife | 0.85~0.95 | 17.00~19.00 | 0.20~0.80 | ≤0.80 | 1.00~1.30 | 0.07~0.12 | ≤0.04 | ≤0.03 | <0.40 | ||
SUS440C | 9Cr18Mo (SUS440C) Hair scissor | 0.95~1.10 | 16.00~18.00 | 0.30~0.70 | ≤0.80 | 0.40~0.70 | ≤0.03 | ≤0.04 | <0.40 | |||
SUS440C or 440F | 11Cr17 (linear guideway) | 0.95~1.2 | 16.00~18.00 | <1.00 | ≤1.00 | <0.75 | ≤0.025 | ≤0.025 | <0.60 | |||
85Cr18Mo2V | 0.80~0.90 | 16.50~18.50 | 0.90~1.40 | ≤0.80 | 2.00~2.50 | 0.30~0.60 | ≤0.03 | ≤0.04 | <0.40 | |||
VG10 | VG10 | 0.95~1.05 | 14.50~15.5 | 0.30~0.50 | ≤0.80 | 0.80~1.20 | 0.25~0.35 | 1.30~1.80 | ≤0.025 | ≤0.025 | <0.50 | |
BG-42 | BG-42 | 1.13~1.20 | 14.5~15.5 | 0.20~0.60 | 0.2~0.4 | 3.95~4.1 | 1.10~1.20 | ≤0.010 | ||||
S35VN | S35VN | 1.32~1.42 | 13.70~14.30 | 0.40~0.60 | 0.40~0.60 | 1.95~2.05 | 2.90~3.10 | ≤0.025 | ≤0.025 | ≤0.25 |
High-end quality for Martensite stainless steel
Professional production of the following martensite stainless steel for high-end quality material of outdoor knife. Kitchen knife, hair scissors etc.
Direction of the industry
Hob broach end milling cutter bit and other metal machine tool processing industry
Kitchen knife
Outdoor knife
Barber Scissors
Hair Scissors
Products been used for SUS440C and VG-10 ,BG-42 제품소개
High temperature bearing M2/9Cr18Mo
고온용 베어링
Automobile engine valve
엔진 벨브
Engine valve port 9Cr18Mo
Product Categories
ZD=ZEICIN PK TAKEFU QUALITY
Metallographic organization comparision
Photo 1 Domestic Industry
Photo 2 Imported From Abroad
Photo 3 Zeicin
Image description: 9Cr18Mo X100 times carbide analysis.
Photo1(Domestic). carbon carbide size Obvious appear big size.
Photo2 (abroad) the carbide distribution is uneven and the individual is large.Reason analysis: during the smelting process, the carbide can not be controlled well. In the late forging, although the forging ratio increases, it fails to make up for the defects of the smelting.
Photo3(ZhengDa=Zeicin) the modification of three technological processes of 1)EAF+LF+VD, 2) Special innovation smelting process of RS ESR, 3) transformation forging of the 9Cr18Mo , So that keep obviously better than the imported ones.The carbide is small and uniform.
Photo 1 Domestic Industry
Photo 2 Imported From Abroad
Photo 3 Zeicin
Image description: 9Cr18Mo X500 times carbide analysis
Photo1(domestic), the carbide individual is obviously large, the processing will appear the phenomenon of detachment.
Photo2(abroad),The carbides are superior to domestic ones, but there are more angular carbide, and cracks and stress concentrations are easy to occur in use, leading to early failure.
Photo3(ZhengDa=Zeicin) the modification of 9Cr18Mo in the process of smelting and forging, the level of carbide is obviously superior to the imports.
Photo 1 Domestic Industry
Photo 2 Imported From Abroad
Photo 3 Zeicin
Image description: 9Cr18Mo X100 times cross section carbide analysis.
Photo1(domestic), Zonal carbides are obvious, the carbide particles are obviously larger than the longitudinal ones, cause analysis: no make modified forging, Just make rolling directly.
Photo2(abroad) the distribution of carbides is not uniform and the individual is large. Reason analysis: during the smelting process, the carbide can not be controlled well. In the late forging, although the forging ratio increases, it fails to make up for the defects of the smelting.
Photo3(ZhengDa=Zeicin) the modification of three technological processes of 1) EAF +LF+VD, 2) Special innovation smelting process of RS ESR, 3) transformation forging of the 9Cr18Mo , So that keep obviously better than the imported ones.The carbide is small and uniform.
SUS440C 조직 분석 Microstructure comparision
Korea SUS440C dia20mm 100times
carbide size:62μm
carbide distribution:3 한국
Korea SUS440C dia20mm 500times
carbide size:62μm
carbide distribution:3 한국
Japan SUS440C dia20mm 100times
carbide size:32μm
carbide distribution:1.5 일본
Japan SUS440C dia20mm 500times
carbide size:32μm
carbide distribution:1.5 일본
Zeicin SUS440C dia20mm 100times
carbide size:12μm
carbide distribution:2 정다몰드
Zeicin SUS440C dia20mm 500times
carbide size:12μm
carbide distribution:2 정다몰드
VG-10 조직 분석 Microstructure comparision
Japan VG-10 dia22mm 100times
carbide size:16μm
carbide distribution:1 일본
Japan VG-10 dia22mm 500times
carbide size:16μm
carbide distribution:1 일본
Zeicin VG-10 dia22mm 100times
carbide size:13μm
carbide distribution:1.5 정다몰드
Zeicin VG-10 dia22mm 500times
carbide size:13μm
carbide distribution:1.5 정다몰드
Takefu 440C
dia3.3X105XLmm 100times
carbide size:17μm
carbide distribution:1.5
Takefu 440C
dia3.3X105XLmm 500times
carbide size:17μm
carbide distribution:1.5
Zhengda=Zeicin VG-10
dia3.3X160XLmm 100times
arbide size:13μm
carbide distribution:1.5
Zhengda=Zeicin VG-10
dia3.3X105XLmm 500times
carbide size:13μm
carbide distribution:1.5
Gloria 440C
dia30mm 100times
carbide size:32μm
carbide distribution:2 .5
Gloria 440C
dia30mm 500times
carbide size:32μm
carbide distribution:2 .5
Zhengda=Zeicin 440C
dia32mm 100times
carbide size:14μm
carbide distribution:2
Zhengda=Zeicin 440C
dia32mm 500times
carbide size:14μm
carbide distribution:2
Martensite stainless steel: 마르텐사이트 스테인레스
The advantages of choosing 9Cr14MoV+Co:
1) It is not easy to break when it is used for warping bending shear;
2) The matrix strength is higher;
3) The toughness is better
For example: one of our representative clients
This company produces for Satellite bearing, which are very influential in China.
http://www.zysbearing.com/
This company is a military enterprise, specializing in the manufacture bear for rockets, satellites etc.. Below test report is from this customer to provice.
This is high temperature bearing used in industry of medical, airplane, high speed rail Which represents a symbol of high-end HSS, In China only our Zhengda=Zeicin company’s quality to achieve customer confirmation to replace imported materials from Japan and Europe, It is also means our quality has been recognized by high-end customers and affirmation
M2
dia35mm 100times microstructure
carbide grain size:8 μm
carbide distribution:2
Customer Feedback
This is one of our Korea custoers who purchase Japan before, but now he would like to purchase from us for the SUS440C and VG10.